Measurement Area 007 from 0010267

Type: Volume Composition

ObjectId: 127967

Created: 5/8/2025 12:41:43 PM by Dudarev Victor gmail [vic.dudarev@gmail.com]

Updated: 9/16/2026 4:27:19 PM by Dudarev Victor gmail [vic.dudarev@gmail.com]

Access: Public Sort Code (asc): 7

License: CC BY 4.0

Description: Automatically created via import from file (MA 007)

[no file attached]

: Co-La-O-V

Composition

ElementAbsolutePercentage
O 90.103 %
V 0.105 %
Co 0.539 %
La 9.253 %

Associated Objects

No associated objects found.

Referenced Objects (Reverse Association)

  • 10246 240313-K3-1
    Sample

    La-Co-V-O hot dep for electrochemistry, 1h preanneal on Si/SiO2 with 50 nm Pt on 10nm Ta, Co: DCXS-750, 70W, V: pulsed DC, 10kHz, 5µs, La2O3: RF, 200W, 20W/min ramp

    Auto
  • 10252 240314-K3-1
    Sample

    La-Co-V-O hot dep 500°C on Sapphire (dsp) for band gap, 1h preanneal Co: DCXS-750, 70W; V: pulsed DC, 60W, 10kHz, 5µs, La2O3: RF, 200W, 20W/min ramp; Problems with pressure controller after 20min, continued with Ar/O2 flow of 40/20sccm, cathodes where shut down and start again to test gas flow values (for La2O3 with ramp of course), same issue after 8min (28min total) so process was canceled

    Auto
  • 10256 240315-K3-1
    Sample

    La-Co-V-O hot dep 500°C on Sapphire (dsp) for band gap, 1h preanneal Co: DCXS-750, 70W; V: pulsed DC, 60W, 10kHz, 5µs, La2O3: RF, 200W, 20W/min ramp

    Auto
  • 10267 240319-K3-1
    Sample

    La-Co-V-O hot deposition 500°C on Sapphire, La2O3: RF, 200W, 20W/min ramp, V: pulsed DC, 10kHz, 5µs, Co: DCXS-750, 70W, preanneal 1h

    Auto

All properties (except table)

Include all template properties
Type Name Value Comment
Int Measurement Area 7 Measurement Area index (1..342) 72109
Float x 4.433 72109
Float y -40.5 72109
String Phases ICSD-7800;ICSD-17668 117085
Float R -3.14829e+007 Ohm 72452