Sapphire

Type: Substrate

ObjectId: 13070

Created: 7/17/2023 7:50:31 PM by Dudarev Victor gmail [vic.dudarev@gmail.com]

Updated: 9/16/2026 4:27:19 PM by Dudarev Victor gmail [vic.dudarev@gmail.com]

Access: Public Sort Code (asc): 0

License: CC BY 4.0

Description:

[no file attached]

Associated Objects

No associated objects found.

Referenced Objects (Reverse Association)

  • 10157 Co-oxide Hot deposition 500°C (homogeneous)
    Sample

    preanneal 500 °C 55 min

  • 10252 240314-K3-1
    Sample

    La-Co-V-O hot dep 500°C on Sapphire (dsp) for band gap, 1h preanneal Co: DCXS-750, 70W; V: pulsed DC, 60W, 10kHz, 5µs, La2O3: RF, 200W, 20W/min ramp; Problems with pressure controller after 20min, continued with Ar/O2 flow of 40/20sccm, cathodes where shut down and start again to test gas flow values (for La2O3 with ramp of course), same issue after 8min (28min total) so process was canceled

  • 10256 240315-K3-1
    Sample

    La-Co-V-O hot dep 500°C on Sapphire (dsp) for band gap, 1h preanneal Co: DCXS-750, 70W; V: pulsed DC, 60W, 10kHz, 5µs, La2O3: RF, 200W, 20W/min ramp

  • 10267 240319-K3-1
    Sample

    La-Co-V-O hot deposition 500°C on Sapphire, La2O3: RF, 200W, 20W/min ramp, V: pulsed DC, 10kHz, 5µs, Co: DCXS-750, 70W, preanneal 1h

  • 10293 240327-K3-1
    Sample

    La-Co-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, V: pulsed DC, 120W, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

  • 10295 240328-K3-1
    Sample

    La-Co-V-O hot deposition 500°C on Sapphire (dsp), La2O3: RF, 200W, 20W/min ramp, V: pulsed DC, 120W, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

  • 10313 240405-K3-1
    Sample

    La-Co-Fe-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, V: pulsed DC, 60W, 10kHz, 5µs, Co: DCXS-750, 70W; Fe: DCSX-1500, 100W; preanneal 1h Water Interlock during pre-annealing, system was completely down, restarted, deposition nwas canceled

  • 10315 240408-K3-1
    Sample

    La-Co-Fe-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, V: pulsed DC, 60W, 10kHz, 5µs, Co: DCXS-750, 70W; Fe: DCSX-1500, 100W; preanneal 1.5h; Water Interlock during process after 20 min, system was completely down, restarted, deposition was canceled, water filter was cleaned

  • 10316 240409-K3-1
    Sample

    La-Co-Fe-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, V: pulsed DC, 60W, 10kHz, 5µs, Co: DCXS-750, 70W; Fe: DCSX-1500, 100W; preanneal 1h

  • 10317 240410-K3-1
    Sample

    La-Co-Fe-V-O hot deposition 500°C for bandgap, La2O3: RF, 200W, 20W/min ramp, V: pulsed DC, 60W, 10kHz, 5µs, Co: DCXS-750, 70W; Fe: DCSX-1500, 100W; preanneal 1h

  • 10408 240619-K5-1
    Sample

    Co-Ni-O hot deposition 500°C (710°C set on PC, 2,25h preanneal) on Sapphire (ssp); Co: MAG2, DC1, 40W; Ni: MAG3, DC2, 70W

  • 10448 240705-K5-1
    Sample

    Co-Ni-O hot deposition 500°C (710°C set on PC, 2h preanneal) on Sapphire (dsp); Co: MAG2, DC1, 40W; Ni: MAG3, DC2, 70W

  • 10466 240711-K5-1
    Sample

    Co-Ni-O hot deposition 500°C (710°C set on PC, 2h preanneal) on Sapphire (ssp); Co: MAG2, DC1, 60W; Ni: MAG3, DC2, 55W

  • 10475 240724-K3-1
    Sample

    500°C hot deposition on Sapphire (ssp), 1h preannealing; Co: DC-750, 70W; Mn: pulsed DC, 100W, 10kHz, 5µs, 20W/min ramp

  • 10478 240725-K3-1
    Sample

    500°C hot deposition on Sapphire (dsp) for band gap, 1h preannealing; Co: DC-750, 70W; Mn: pulsed DC, 100W, 10kHz, 5µs, 20W/min ramp

  • 10480 240729-K3-1
    Sample

    500°C hot deposition on Sapphire (ssp), 1h preannealing; Co: DC-750, 70W; Mn: pulsed DC, 100W, 10kHz, 5µs, 20W/min ramp, Ni: DCXS-1500, 70W

  • 10481 240730-K3-1
    Sample

    500°C hot deposition on Sapphire (dsp) for band gap, 1h preannealing; Co: DC-750, 70W; Mn: pulsed DC, 100W, 10kHz, 5µs, 20W/min ramp, Ni: DCXS-1500, 70W

  • 10484 240801-K3-1
    Sample

    500°C hot deposition on Sapphire (ssp), 1h preannealing; Co: DC-750, 70W; Mn: pulsed DC, 100W, 10kHz, 5µs, 20W/min ramp, Fe: DCXS-1500, 60W

  • 10486 240802-K3-2
    Sample

    500°C hot deposition on Sapphire (dsp) for band gap, 1h preannealing; Co: DC-750, 70W; Mn: pulsed DC, 100W, 10kHz, 5µs, 20W/min ramp, Fe: DCXS-1500, 60W

  • 10491 240807-K3-1
    Sample

    500°C hot deposition on Sapphire (ssp), 1h preannealing; Co: DC-750, 70W; Mn: pulsed DC, 100W, 10kHz, 5µs, 20W/min ramp, Fe: DCXS-1500, 70W, Ni: RF, 140W

  • 10492 240808-K3-1
    Sample

    500°C hot deposition on Sapphire (ssp), 1h preannealing; Co: DC-750, 70W; Mn: pulsed DC, 100W, 10kHz, 5µs, 20W/min ramp, Fe: DCXS-1500, 70W, Ni: RF, 210W

  • 10493 240809-K3-1
    Sample

    500°C hot deposition on Sapphire (dsp) for bandgap, 1h preannealing; Co: DC-750, 70W; Mn: pulsed DC, 100W, 10kHz, 5µs, 20W/min ramp, Fe: DCXS-1500, 70W, Ni: RF, 210W

  • 10667 241105-K3-1
    Sample

    La-Co-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 10kHz, 5µs, Co: DCXS-750, 70W, preanneal 1h

  • 10669 241106-K3-1
    Sample

    La-Co-V-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

  • 10670 241107-K3-1
    Sample

    La-Co-V-O hot deposition 500°C onn Sapphire (dsp) for band gap, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, preanneal 1h

  • 10674 241111-K3-1
    Sample

    La-Co-Fe-Ni-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, Ni: 70W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, Fe: DCSX-1500, 100W, preanneal 1h

  • 10677 241113-K3-1
    Sample

    La-Co-Fe-Ni-O hot deposition 500°C, La2O3: RF, 200W, 20W/min ramp, Ni: 100W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, Fe: DCSX-1500, 100W, preanneal 1h

  • 10678 241114-K3-1
    Sample

    La-Co-Fe-Ni-O hot deposition 500°C for band gap, La2O3: RF, 200W, 20W/min ramp, Ni: 100W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, Fe: DCSX-1500, 100W, preanneal 1h

  • 10698 241126-K3-1
    Sample

    Co-O hot dep, 500°C, 20rpm, Co: 70W pulsed DC, 350kHz, 1.4µs

  • 10727 241203-K3-1
    Sample

    Co-O hot dep, 500°C, 20rpm, Co: 70W DC

  • 11081 250808-K3-1
    Sample

    Co-Ni-O RT, Ni: 100W, pulsed DC, 350kHz, 1.4µs, Co: DCXS-750, 70W, 40sccm Ar 20sccm O2

  • 11642 260710-K3-1
    Sample

    Co-O deposition on Sapphire at RT for post annealing

  • 11647 260715-K3-1
    Sample

    Co-O on Sapphire, homogeneous film around 100 nm thickness for Mahyar/Dylan

  • 11648 260716-K3-1
    Sample

    Co-O deposition at RT on Sapphire, thickness gradient from around 150 - 300 nm thickness for Mahyar/Dylan

  • 11708 260827-K3-1
    Sample

    Co-O hot dep, 700°C (heater setpoint), 20rpm, Co: 70W DC; Test of the new heater

  • 11712 260831-K3-1
    Sample

    Co-O hot dep, 900°C (heater setpoint), 20rpm, Co: 70W DC; Test of the new heater

  • 11716 260902-K3-1
    Sample

    Co-O hot dep, 950°C (heater setpoint), 20rpm, Co: 70W DC; Test of the new heater; actual temperature indicated by the heater: 932°C

  • 11721 260903-K3-1
    Sample

    Co-O hot dep, 950°C (heater setpoint), 20rpm, Co: 70W DC; Test of the new heater; Sr/O2 80/40; actual temperature indicated by the heater: 910°C

  • 11729 260908-K3-1
    Sample

    Co-O on MgO (on Sapphire carrier wafer), homogeneous film around 100 nm thickness for Mahyar/Dylan

  • 6758 Sample MSE Ag-Pd-Ru
    Sample

    Sample for MSE (Ag-Pd-Ru at Sapphire, ID=0006758, K7) by Banko Lars.

  • 7033 Sample MSE Ag-Pd-Pt
    Sample

    Sample for MSE (Ag-Pd-Pt at Sapphire, ID=0007033, K7) by Banko Lars.

  • 11081 250808-K3-1_2
    Sample

    Annealing at 700°C, 12h

All properties (except table)

No properties found

The table

   Download properties in Excel

No properties for rendering in a table found